Steel wire braided rubber hoses can transport raw materials with a certain working pressure and temperature, and paying attention to their application is a factor in ensuring normal operation.

1. When the operating temperature of the application is high, the service life of high-pressure hoses is short, so it is important to avoid heat sources as much as possible. Using armored cable hoses or installing insulation materials is a good solution.

2. During installation and use, it is necessary to avoid contact with other pipelines to prevent friction and cracking. In the case of cross cutting or work that may generate friction, protective equipment (pipe clamps/springs) should be used.

3. When bending is required, the bending radius r of the product is greater than (9-10) D (D is the diameter of the hose), and the parallel line segment from the joint to the gradually bending exceeds 6 times the diameter of the pipeline.

4. The installation and application of steel wire braided rubber hoses should not be too straight, but should have a certain length capacity. There is no relative speed between the two parties, so it is necessary to keep the rubber hose loose. When the rubber hose is subjected to force, its length and diameter will change, so it will expand under tight working pressure, resulting in a decrease in compressive strength.

5. Prevent deformation during the entire installation process. When the hose deforms, it is likely to reduce its compressive strength or loosen the joint.

6. The bending of the hose and the hose joint should be installed on the same plane to avoid deformation. In special circumstances, if the joints on both sides of the hose need to be on two different plans, buckles should be installed at appropriate positions to divide the hose into two parts, so that each part is on the same plan.

7. If the rubber hose is installed on important components, it is recommended to perform regular maintenance or replacement.

From a quality perspective, whether the product has achieved positive sulfurization can be expressed in the form of under sulfur or over sulfur. Failure to properly sulfurize can result in substandard product characteristics, asymmetric wall thickness of the rubber hose, and significant damage to the inner rubber layer.

If the steel wire braided rubber hose or coiled steel wire high-pressure rubber hose fails to follow the production process, the braiding angle does not reach 54 degrees and 44 minutes, and the braided steel wire is too tight or too loose, it will cause deformation during product application. The poor tightness of the inner adhesive layer can easily allow substances to enter the steel wire layer, resulting in insufficient adhesion between the steel wire layer and the adhesive. Low sealing performance can cause rusting of the steel wire.